Light Mullite M1.2 /3-5mm
Light weight aggregate
Al2O3: 65%min
Fe2O3:1.6%max
Refractoriness:1750 min
Compressive strength :18-20Mpa
MaterialsBrandMain chemical compositionRefractoriness/°Ccompressive strength/MpaAl2O3Mullite...
pigment kaolin powder
1 Whiteness: 90-95%
2 origin: Shanxi,China
3 AL2O3: 45+/-2%
4 SIO2: 52+/-2%
5 mesh size: 200/325/800/1250mesh
specificationJTKA-01Whiteness (%)≥91Particle size(-10μm,%)≥97Residue on 325 mesh (%)≤0.006Oil absorption(g/100g)40-50PH6.0-8.0Water content...
kaolin clay for ceramic
AL2O3: 45% min
SIO2: 47-48%
FE2O3: 1.2% max
Bulk density: 2.4-2.5g/cm3
Moisture: 0.5%
AL2O3: 45% minSIO2: 47-48%FE2O3: 1.2% maxBulk density: 2.4-2.5g/cm3Moisture: 0.5%
kaolin clay for...
ceramic proppant
1. high conductivity and strength
2. low acid and turbidity
3. own ore
4. competitive price
ItemSizeRoundnessSphericityBulk density(g/m3)Apparent density(g/m3)Turbidity(%)Acid Solubility(12%Hcl+3%HF)%Crush resistance(%)52Mpa69Mpa86MpaLow...
Refractory grade White fused alumina
1. Al2O3 : 99%min
2. Fe2O3: 0.15% max
3. SiO2: 0.15%max
4.Abrasive/refractory
5. Size: grain or powder
SpecificationstandardAl2O3(%)≥99Fe2O3(%)≤0.15SiO2(%)≤0.15k2O +Na2O(%)≤0.45WFA is designed for general industrial use in operations such as lapping,...
ceramic kaolin
1. ceramic kaolin clay calcined
2. AL2O3: 45% min
3. SIO2: 48-50%
4. FE2O3: 0.8% max
5. Bulk density: 2.4-2.5g/cm3
SpecificationstandardSiO2(%)48-50Fe2O3(%)≤0.8Al2O3(%)≥45TiO2(%)≤2.0Bulk density(g/cm3)≥2.4
...
Refractory grade White fused alumina
1. Al2O3 : 99%min
2. Fe2O3: 0.15% max
3. SiO2: 0.15%max
4.Abrasive/refractory
5. Size: grain or powder
SpecificationstandardAl2O3(%)≥99Fe2O3(%)≤0.15SiO2(%)≤0.15k2O +Na2O(%)≤0.45WFA is designed for general industrial use in operations such as lapping,...